Anti Fog Coating
|
|
| |
For Details, Click Here to Send Us an Inquiry At: sales@epoxy-paint.cn to see if this High Temperature or Heat Resistant Coatings is right for your application. |
| |
 |
| |
|
Advantages:
- Better fog resistant features
- Better optical visibility
- More abrasion resistant
- High end dipping and spraying processes
- Much more cost competitive
- More custom flexible
Honest Joy Anti Fog Coating (AFC) Polycarbonate Sheet and Film Options
|
Thickness (mm)
|
Width (mm)
|
Length (mm)
|
Remark
|
|
0.125
|
930
|
400,000
|
Optical Grade
|
|
0.15
|
930
|
350,000
|
Optical Grade
|
|
0.25
|
930
|
300,000
|
Optical Grade
|
|
0.3
|
930
|
300,000
|
Optical Grade
|
|
0.5
|
930
|
160,000
|
Optical Grade
|
|
0.5
|
915
|
1,830
|
Optical Grade
|
|
0.6
|
915
|
1,830
|
Optical Grade
|
|
0.7
|
915
|
1,830
|
Optical Grade
|
|
0.8
|
915
|
1,830
|
Optical Grade
|
|
1
|
915
|
1,830
|
Optical Grade
|
|
1.5
|
1,220
|
1,830
|
Optical Grade
|
|
2
|
1,220
|
1,830
|
Optical Grade
|
|
3
|
1,220
|
1,830
|
Optical Grade
|
|
4
|
1,220
|
1,830
|
Optical Grade
|
|
6
|
1,220
|
1,830
|
Clear
|
|
8
|
1,220
|
1,830
|
Clear
|
|
10
|
1,220
|
1,830
|
Clear
|
|
12
|
1,220
|
1,830
|
Clear
|
-
- Honest Joy can customize dimensions based on your requirement for anti fog coating.
Honest Joy Anti Fog Coating (AFC) Polycarbonate Sheet Technical Data:
|
Item
|
Property
|
Test Method
|
U/ M
|
Value
|
|
|
|
|
|
|
|
|
Diopter
|
ECE 22.05
|
D
|
<0.125
|
|
Haze
|
ASTM D 1003
|
%
|
0.37
|
|
Fog Free time
|
ECE22.05/ECE324
|
s
|
>22
|
|
Fog Free time
|
Freezing Test
|
s
|
no fogging
|
|
|
|
|
|
|
|
Mechanical
|
Hardness 1KG
|
ANSI Z87.1 2010
|
H
|
1
|
|
High velocity impact
|
ANSI Z87.1 2010
|
ft/s
|
>300
|
|
Cross-Cut tape test
|
ANSI Z87.1 2010
|
NA
|
Pass
|
|
Elongation, yield % 7
|
ANSI Z87.1 2010
|
%
|
7
|
|
Elongation, break ISO 527 % 110
|
ANSI Z87.1 2010
|
%
|
110
|
|
Tensile stress, yield
|
ANSI Z87.1 2010
|
Mpa
|
60
|
|
Tensile modulus MPa
|
ANSI Z87.1 2010
|
Mpa
|
2300
|
|
Flexural strength, yield
|
ANSI Z87.1 2010
|
Mpa
|
100
|
|
Flexural modulus ISO 178 MPa 2500
|
ANSI Z87.1 2010
|
Mpa
|
2500
|
|
Izod notched impact, 20 °C
|
ANSI Z87.1 2010
|
KJ/m²
|
65
|
|
|
|
|
|
|
|
Physical
|
Gravity
|
ANSI Z87.1 2010
|
g/cm³
|
1.2
|
|
Water absorption, 24 hours
|
ANSI Z87.1 2010
|
%
|
0.15
|
|
|
|
|
|
|
|
Thermal
|
Mold shrinkage
|
ANSI Z87.1 2010
|
%
|
0.5-0.7
|
|
Thermal expansion
|
ANSI Z87.1 2010
|
1/ °C
|
7x10-5
|
|
Vicat Softening Temp., Rate B /
120(base sheet)
|
ANSI Z87.1 2010
|
°C
|
150
|
|
HDT, 0.45 MPa
|
ANSI Z87.1 2010
|
°C
|
138
|
|
|
| |
| |
|
| |
|
| |
|
|
| | |
|
|